Zirconia 3D Multilayer Disk Zirconia Dental Blanks

• Usage：Planting Material, Denture Processing
• Usage Times：Disposable
• Material：Ceramics
• Applicable Departments：Dental Department
• Nature：Denture Processing
• Certification：CE, FDA Sfds Rfda

=== Base Info ===

• Model NO.：HT, ST, UT, UT-S, ST-C, ST-M, UT-M, 3D Multilayer
• Color：Vita 16 Color
• Strength：1100-1350 MPa
• Transmittance：30%-49%
• Sintering Temperaure：1530
• Sample Provided：Yes
• Transport Package：Carton
• Specification：20*20*10 cm
• Trademark：KINGCH
• Origin：Hebei Province China
• Production Capacity：200000

=== Description ===
   Item       HS      HT       ST      ST-C     ST-M   UT-M       UT    3D multilayer  Flexural  Strength  1470Mpa 1470 Mpa1200 Mpa 1200 Mpa  1200 Mpa 1100 Mpa1100 Mpa >1200MpaTransmittance   Opaque    30%    41%     40%     40%     45%     45%      49%Density  pre sintering  (g/cm3)     3.20     3.20    3.15     3.20     3.20    3.25    3.25      3.25Vicker's Hardness (Mpa)     1400    1400   1300    1350    1350    1250    1250     1250Shrinkage Factor(%)    19-22    19-22   19-22   19-22   19-22   19-22   19-22    19-22Sintering Temperature    1460 ºC    1460 ºC  1530 ºC   1530 ºC   1530 ºC  1530 ºC  1530 ºC  1480 ºC